牌號(hào)
|
E460R低合金結(jié)構(gòu)鋼熱軋鋼板
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
中國(guó)ISC
|
L04604
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
GB /T 3274-2017
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
碳素結(jié)構(gòu)鋼和低合金結(jié)構(gòu)鋼熱軋鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Hot-rolled plates, sheets and strips of carbon structural steels and high strength low alloy structural sheets
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
品牌/供貨源
|
中國(guó)大陸-> 寶鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類
|
合金鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
強(qiáng)度?焊接性
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
標(biāo)簽
|
熱軋鋼板和鋼帶?低合金結(jié)構(gòu)鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
說明
|
性能特點(diǎn)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
與Q420相比，Q460D鋼的強(qiáng)度更高，經(jīng)正火、正火加回火或淬火加回火處理后有很高的綜合力學(xué)性能，Q460D鋼具有良好的韌性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
用途舉例
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
屬于備用鋼種。主要用于各種大型工程結(jié)構(gòu)及要求強(qiáng)度高、載荷大的輕型結(jié)構(gòu)。廣泛用于各類工程機(jī)械、如礦山和各類工程施工用的鉆機(jī)、電鏟、電動(dòng)反斗車、礦用汽車、挖掘機(jī)、裝載機(jī)、推土機(jī)、各類起重機(jī)、煤礦液壓支架等機(jī)械設(shè)備及其他結(jié)構(gòu)件。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
本標(biāo)準(zhǔn)適用于厚度不大于400mm的碳素結(jié)構(gòu)鋼和低合金鋼熱軋鋼板和鋼帶
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
E460R?化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
N
|
Ti
|
V
|
Nb
|
B
|
Al?b
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.015
|
|
最大值
|
0.2
|
0.6
|
1.8
|
0.03
|
0.025
|
0.3
|
0.8
|
0.55
|
0.2
|
0.015
|
0.2
|
0.2
|
0.11
|
0.004
|
-
|
|
鋼的牌號(hào)和化學(xué)成分(熔煉分析)應(yīng)符合GB/T 700和GB/T 1591的規(guī)定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
b當(dāng)采用全鋁（Alt）含量表示時(shí)，Alt應(yīng)不小于0.02%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
E460R?機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
厚度（直徑，邊長(zhǎng)）
|
抗拉強(qiáng)度
|
屈服點(diǎn)
|
斷后伸長(zhǎng)率或延伸率
|
|
|
|
|
|
|
|
|
|
|
|
|
|
t
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
|
|
|
|
|
|
|
mm
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
t≤16
|
550~720
|
≥460
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
|
|
16
|
550~720
|
≥440
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
|
|
40＜t≤63
|
550~720
|
≥420
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
63＜t≤100
|
550~720
|
≥400
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
100＜t≤150
|
530~700
|
≥380
|
≥16
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1、力學(xué)性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
①厚度小于3mm的鋼板和鋼帶的抗拉強(qiáng)度和斷后伸長(zhǎng)率應(yīng)符合GB/T 700、GB/T 1591的規(guī)定，斷后伸長(zhǎng)率允許比GB/T 700或GB/T 1591的規(guī)定降低5%(絕對(duì)值)。根據(jù)需方要求，鋼板和鋼帶的屈服強(qiáng)度可按GB/T 700、GB/T 1591的規(guī)定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
②厚度不小于3mm的鋼板和鋼帶的力學(xué)和工藝性能應(yīng)符合GB/T 700、GB/T 1591的規(guī)定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2、工藝性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
鋼板和鋼帶應(yīng)做180°彎曲試驗(yàn)，試樣彎曲壓頭直徑應(yīng)符合GB/T 700、GB/T 1591的規(guī)定。如供方能保證冷彎試驗(yàn)合格，可不作檢驗(yàn)。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|